| 详细介绍： (1)尺寸规格
塑料模具用扁钢的尺寸规格
宽度/mm
|
厚 度／mm
|
25
|
30
|
37
|
40
|
45
|
55
|
68
|
75
|
85
|
95
|
105
|
理论质量／(kg／m)
|
170
|
33.36
|
40.04
|
49.38
|
53.38
|
60.05
|
73.40
|
90.75
|
100.09
|
113.43
|
126.78
|
140.12
|
190
|
37.28
|
44.75
|
55.19
|
59.66
|
67.12
|
82.03
|
101.42
|
111.86
|
126.78
|
141.69
|
156.60
|
210
|
41.21
|
49.46
|
60.99
|
65.94
|
74.18
|
90.67
|
112.10
|
123.64
|
140.12
|
156.61
|
173.09
|
230
|
45.14
|
54.17
|
66.80
|
72.22
|
81.25
|
99.30
|
122.77
|
135.41
|
153.47
|
171.52
|
189.58
|
260
|
51.03
|
61.23
|
75.52
|
81.64
|
91.85
|
112.26
|
138.79
|
153.08
|
173.49
|
193.89
|
214.31
|
280
|
54.95
|
65.94
|
81.33
|
87.92
|
98.91
|
120.89
|
149.46
|
164.85
|
186.83
|
208.81
|
230.79
|
300
|
58.88
|
70.65
|
87.14
|
94.20
|
105.98
|
129.53
|
160.14
|
176.63
|
200.18
|
223.72
|
247.28
|
325
|
63.78
|
76.54
|
94.40
|
102.05
|
114.81
|
140.32
|
173.49
|
191.34
|
216.86
|
242.37
|
267.88
|
365
|
71.63
|
85.96
|
106.01
|
114.61
|
128.94
|
157.59
|
194.84
|
214.89
|
243.55
|
272.20
|
300.85
|
390
|
76.54
|
91.85
|
113.28
|
122.46
|
137.77
|
168.38
|
208.18
|
229.61
|
260.23
|
290.84
|
321.46
|
410
|
80.46
|
96.56
|
U9.08
|
128.74
|
144.83
|
177.02
|
218.86
|
241.39
|
272.57
|
305.76
|
337.94
|
注：1．表中理论质量按密度为7.85g／cm3计算。
2．扁钢的通常长度为2-6m。
(2)允许偏差
塑料模具用扁钢的允许偏差 (mm)
轧制扁钢
|
锻制扁钢
|
宽 度
|
厚 度
|
宽 度
|
厚 度
|
尺 寸
|
允许偏差
|
尺寸
|
允许偏差
|
尺寸
|
允许偏差
|
尺寸
|
允许偏差
|
170-410
|
±2％
(最大值不
超过±6)
|
25-55
|
±1.2
|
170-210
|
±5
|
≤65
|
±2.5
|
>55-85
|
±1.5
|
>210-
410
|
协议
|
>65-105
|
协议
|
>85-105
|
±2.5
|
注：根据需方要求可供应全正偏差钢材，其偏差值为正负偏差绝对值之和。
扁钢截面形状不正的最大允许值(c值) (mm)
扁钢厚度
|
最大允许尺寸(c值)
|
25～55
|
3.5
|
>55
|
协议
|
(3)牌号和化学成分
(4)交货状态
(1)非合金塑料模具扁钢以热轧状态交货，合金塑料模具扁钢以退火状态交货。
(2)根据需方要求，经供需双方协议，SM3Cr2Mo、SM3Cr2Ni1Mo、SM2Cr13可供应预硬化状态钢材。
(5)力学性能
塑料模具用扁钢的牌号和化学成分
钢类
|
牌 号①
|
化学成分(质量偏差)(％)
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
其他
|
≤
|
非合
金钢
|
SM45
|
0.42-0.48
|
0.17-0.37
|
0.50-0.80
|
0.030
|
0.030
|
|
|
|
|
SM50
|
0.47-0.53
|
0.17-0.37
|
0.50-0.80
|
0.030
|
0.030
|
|
|
|
|
SM55
|
0.52-0.58
|
0.17-0.37
|
0.50-0.80
|
0.030
|
0.030
|
|
|
|
|
合
金
钢
|
SM1CrNi3
|
0.05-0.15
|
0.10-0.40
|
0.35-0.75
|
0.030
|
0.030
|
1.25-1.75
|
3.25-3.75
|
|
|
SM3Cr2Mo
|
0.28-0.40
|
0.20-0.80
|
0.60-1.00
|
0.030
|
0.030
|
1.40-2.00
|
|
0.30-0.55
|
|
SM3Cr2NiMo
|
0.32-0.42
|
0.20-0.80
|
1.00-1.50
|
0.030
|
0.030
|
1.40-2.00
|
0.80-1.20
|
0.30-0.55
|
|
SM2CrNi3MoA11S
|
0.20-0.30
|
0.20-0.50
|
0.50-0.80
|
0.030
|
0.100
|
1.2-1.8
|
3.0-4.0
|
0.20-0.40
|
A11.0-1.6
|
SM4Cr5MoSiV
|
0.33-0.43
|
0.80-1.25
|
0.20-0.60
|
0.030
|
0.030
|
4.75-5.50
|
|
1.10-1.60
|
V0.30-0.60
|
SM4Cr5MoSiV1
|
0.32-0.45
|
0.80-1.25
|
0.20-0.60
|
0.030
|
0.030
|
4.75-5.50
|
|
1.10-1.75
|
V0.80-1.20
|
SMCr12Mo1V1
|
1.40-1.60
|
0.10-0.60
|
0.10-0.60
|
0.030
|
0.030
|
11.00-13.00
|
|
0.70-1.20
|
V0.50-1.10
|
SM2Cr13
|
0.16-0.25
|
≤1.00
|
≤1.00
|
0.030
|
0.030
|
12.00-14.00
|
②
|
|
|
SM3Cr17Mo
|
0.28-0.35
|
≤0.80
|
≤1.00
|
0.030
|
0.030
|
16.00-18.00
|
②
|
0.75-1.25
|
|
SM4Cr13
|
0.35-0.45
|
≤0.60
|
≤0.80
|
0.030
|
0.030
|
12.00-14.00
|
②
|
|
|
注：钢中残余铜、镍含量(质量分数)各不大于0.25％。
①“SM”代表塑料模具中“塑模”两汉字汉语拼音首位字母。
②允许含有小于或等于0.60％镍。
塑料模具用扁钢的硬度
牌 号
|
退火硬度
HBS
≤
|
淬回火硬度
|
淬 火
|
回 火
|
硬度≥
|
HRC
|
HBS
|
SM45
|
一般以热轧状态交货，布氏硬度HBS为155～215
|
SM50
|
一般以热轧状态交货，布氏硬度HBS为165～225
|
SM55
|
一般以热轧状态交货，布氏硬度HBS为170～230
|
SM1CrNi3
|
212
|
①
|
①
|
①
|
①
|
SM3Cr2Mo
|
235
|
850～880℃油冷
|
550～600℃空冷
|
30
|
|
SM3Cr2Ni1Mo
|
250
|
850～880℃油冷
|
550～650℃空冷
|
32
|
|
SM2CrNi3MoA11
|
235
|
850～900℃油冷
|
510～530℃空冷②
|
40
|
|
SM4Cr5MoSiV
|
235
|
1000～1200℃空冷
|
540～560℃空冷③
|
53
|
|
SM4Cr5MoSiV1
|
235
|
1000～1200℃空冷
|
540～560℃空冷③
|
53
|
|
SMCr12Mo1V1
|
255
|
1003～1200℃空冷
|
190～21O℃空冷
|
59
|
|
SM2Cr13
|
223
|
920～980℃油冷
|
600～750℃空冷
|
|
192
|
SM3Cr17Mo
|
223
|
1000～1050℃油冷
|
200～300℃空冷
|
43
|
|
SM4Cr13
|
201
|
1050～1100℃油冷
|
200～300℃空冷
|
50
|
|
①渗碳钢不做淬回火硬度试验。
②时效时间为8～10h。
③回火两次。
塑料模具用扁钢的力学性能
牌 号
|
推荐热处理制度
|
ób／MPa
|
ós／MPa
|
δ5(％)
|
Ψ(％)
|
Ak(u)／J
|
≥
|
SM45
|
820-870℃空冷
|
600
|
355
|
16
|
40
|
|
SM50
|
810-860℃空冷
|
630
|
375
|
14
|
40
|
|
SM55
|
800-850℃空冷
|
645
|
380
|
13
|
35
|
|
SM3Gr2Mo
|
850-880℃
550-650℃油冷+空冷
|
960
|
800
|
10
|
35
|
40
|
SM3Cr2-Ni1Mo
|
850-880℃
550-650℃油冷+空冷
|
980
|
800
|
10
|
35
|
45
|
SM2Cr13
|
920-980"C油冷+水冷
600-750℃
|
635
|
440
|
20
|
50
|
63
|
(6)用途
塑料模具钢的特性和应用
牌 号
|
特性和应用
|
SM45
|
价格低廉、机械加工性能好，用于日用杂品、玩具等塑料制品的模具
|
SM50
|
硬度比SM45高，用于性能要求一般的塑料模具
|
SM55
|
淬透性、强度比SM50高，用于较大型的、性能要求一般的塑料模具
|
SM1CrNi3
|
塑性好，用于需冷挤压反印法压出型腔的塑料模具制作
|
SM3Cr2Mo
|
预硬化钢，用于型腔复杂，要求镜面抛光的模具
|
SM3Cr2Ni1Mo
|
预硬化钢，淬透性比SM3Cr2Mo高，用于大型精密塑料模具
|
SM2CrNi3MoA11
|
析出硬化钢，用于型腔复杂的精密塑料模具
|
SM4CrSMoSiV
|
强度高、韧性好，用于玻璃纤维、金属粉末等复合强化塑料成型用模具
|
SM4Cr5MoSiV1
|
热稳定性、耐磨性比SM4Cr5MoSiV高，用于工程塑料、键盘等的模具制作
|
SMCr12Mo1V1
|
硬度高、耐磨，用于齿轮、微型开关等精密模具
|
SM2Cr13
|
耐腐蚀，用于耐蚀母模、托板、安装板等模具
|
SM3Cr17Mo
|
耐腐蚀，用于PVC等腐蚀性较强的塑料成型模具
|
SM4Cr13
|
耐腐蚀、耐磨、抛光性好，用于唱片、透明罩等精密模具
|
8.热轧等边角钢（GB／T9787--1
| 
放大图片