TYPICAL PROPERTIES (1)
|
|
MECHANICAL/机械性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 5 mm/min
|
69
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 5 mm/min
|
66
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 5 mm/min
|
4
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 5 mm/min
|
5
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 5 mm/min
|
3100
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
|
115
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
|
3200
|
MPa
|
ASTM D 790
|
|
Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg
|
75
|
mg/1000cy
|
SABIC Method
|
|
Tensile Stress, yield / 抗张程度,屈服, 5 mm/min
|
58
|
MPa
|
ISO 527
|
|
Tensile Stress, break / 抗张程度,断裂, 5 mm/min
|
55
|
MPa
|
ISO 527
|
|
Tensile Strain, yield / 拉伸伸长,屈服, 5 mm/min
|
4
|
%
|
ISO 527
|
|
Tensile Strain, break / 拉伸伸长,断裂, 5 mm/min
|
5
|
%
|
ISO 527
|
|
Tensile Modulus / 拉伸模量, 1 mm/min
|
3100
|
MPa
|
ISO 527
|
|
Flexural Stress, break / 弯曲强度,断裂, 2 mm/min
|
100
|
MPa
|
ISO 178
|
|
Flexural Modulus / 挠曲模量, 2 mm/min
|
3000
|
MPa
|
ISO 178
|
|
Hardness / 硬度, H358/30
|
140
|
MPa
|
ISO 2039-1
|
|
IMPACT/冲击性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
|
50
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度, -30°C
|
55
|
J/m
|
ASTM D 256
|
|
Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C
|
8
|
J
|
ASTM D 3763
|
|
Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 +23°C
|
35
|
kJ/m²
|
ISO 180/1U
|
|
Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*4 -30°C
|
30
|
kJ/m²
|
ISO 180/1U
|
|
Charpy（简支梁缺口冲击强度） 23°C, Unnotch（无缺口） Edgew 80*10*4 sp=62mm
|
40
|
kJ/m²
|
ISO 179/1eU
|
|
Charpy（简支梁缺口冲击强度） -30°C, Unnotch（无缺口） Edgew 80*10*4 sp=62mm
|
40
|
kJ/m²
|
ISO 179/1eU
|
|
THERMAL/热性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
140
|
°C
|
ASTM D 1525
|
|
HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
120
|
°C
|
ASTM D 648
|
|
CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）
|
6.6E-05
|
1/°C
|
ASTM E 831
|
|
CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）
|
5.2E-05
|
1/°C
|
ASTM E 831
|
|
Thermal Conductivity / 导热系数
|
0.28
|
W/m-°C
|
ISO 8302
|
|
CTE（线形膨胀系数）, 23°C to 80°C, flow（流动）
|
5.E-05
|
1/°C
|
ISO 11359-2
|
|
CTE（线形膨胀系数）, 23°C to 80°C, xflow（横向）
|
6.E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Ball Pressure Test, approximate maximum
|
125
|
°C
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 A/50
|
140
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
130
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120
|
140
|
°C
|
ISO 306
|
|
HDT（热变形温度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
115
|
°C
|
ISO 75/Ae
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
50
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
50
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
50
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Specific Gravity / 比重
|
1.13
|
-
|
ASTM D 792
|
|
Mold Shrinkage on Tensile Bar / 收缩率, flow（流动） (2)
|
0.3 - 0.5
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm
|
0.3 - 0.5
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 300°C/5.0 kgf
|
24
|
g/10 min
|
ASTM D 1238
|
|
Density / 密度
|
1.25
|
g/cm³
|
ISO 1183
|
|
Water Absorption / 吸水率, (23°C/sat)
|
0.45
|
%
|
ISO 62
|
|
Moisture Absorption / 吸水率, 平衡 (23°C / 50% RH)
|
0.06
|
%
|
ISO 62
|
|
Melt Volume Rate / 溶化体积流率, MVR at 280°C/5.0 kg
|
10
|
cm³/10 min
|
ISO 1133
|
|
ELECTRICAL/电气性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Volume Resistivity / 体积电阻率
|
1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity ROA / 表面电阻率
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, in oil / 耐电强度，在油中, 0.8 mm
|
33
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil / 耐电强度，在油中, 1.6 mm
|
26
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm
|
16
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity / 相对介电常数, 50/60 Hz
|
3
|
-
|
IEC 60250
|
|
Relative Permittivity / 相对介电常数, 1 MHz
|
2.9
|
-
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.006
|
-
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.003
|
-
|
IEC 60250
|
|
Comparative Tracking Index / 相比耐漏电起痕指数
|
175
|
V
|
IEC 60112
|
|
FLAME CHARACTERISTICS/火焰特性
|
value/值
|
Unit/单位
|
Standard/标准
|
|
UL Recognized, 94V-1 Flame Class Rating / 阻燃等级 (3)
|
1.2
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)
|
1.5
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3)
|
3
|
mm
|
UL 94
|
|
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at
|
3.2
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index / 极限氧指数 (LOI)
|
32
|
%
|
ISO 4589
|