| 详细介绍：
沙伯基础PPO FN150X
联系人李生
联系电话13480060007或QQ2578981340
邦懋塑胶为您提供详细的Noryl PPO FN150X物性表参数。
想了解更多的与Noryl PPO FN150X相关的物性参数，
如果您对我们的Noryl PPO有任何疑问，或者想索取物性表datasheet、物质安全资料证书MSDS、ROHS检验报告、SGS报告请来电
NORYL PPO FN150X物性表
改良的可靠性与生产率。薄壁性能。 UL94 V-0/5VA额定。试样厚度0.250"，20%减重的数据。
相关色号：FN150X-GY6C356、FN150-GY4722
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL机械性能
|
value
|
Unit
|
Standard
|
|
FOAM - MECHANICAL机械性能 6.4 mm Wt Reduction
|
20
|
%
|
-
|
|
Tensile Stress, yield / 抗张程度，屈服, 6.35 mm
|
28
|
MPa
|
ASTM D 638
|
|
Tensile Stress, break, 6.35 mm
|
28
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yield, 6.35 mm
|
7.3
|
%
|
ASTM D 638
|
|
Tensile Strain, break, 6.35 mm
|
14
|
%
|
ASTM D 638
|
|
Flexural Stress, yield, 6.4 mm
|
52
|
MPa
|
ASTM D 790
|
|
Flexural Modulus, 6.4 mm
|
1740
|
MPa
|
ASTM D 790
|
|
Hardness, Rockwell R / 硬度, 洛氏 R
|
121
|
-
|
ASTM D 785
|
|
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg
|
152
|
mg/1000cy
|
ASTM D 1044
|
|
IMPACT
|
value
|
Unit
|
Standard
|
|
FOAM - IMPACT 6.4 mm Wt Reduction
|
20
|
%
|
-
|
|
Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C, 6.4mm
|
341
|
J/m
|
ASTM D 4812
|
|
THERMAL
|
value
|
Unit
|
Standard
|
|
FOAM - THERMAL 6.4mm Wt Reduction
|
20
|
%
|
-
|
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
110
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed / 热变形温度，0.45 MPa, 6.4 mm, 未退火
|
89
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed / 热变形温度，1.82 MPa, 6.4 mm, 未退火
|
73
|
°C
|
ASTM D 648
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
50
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
50
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
50
|
°C
|
UL 746B
|
|
PHYSICAL
|
value
|
Unit
|
Standard
|
|
FOAM - PHYSICAL 6.4mm Wt Reduction
|
20
|
%
|
-
|
|
Specific Gravity/比重
|
1.12
|
-
|
ASTM D 792
|
|
Water Absorption, 24 hours / 吸水率， 24小时
|
0.06
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow, 6.4 mm
|
0.6 - 0.8
|
%
|
SABIC Method
|
|
Mold Shrinkage, xflow, 6.4 mm
|
0.6 - 0.8
|
%
|
SABIC Method
|
|
FLAME CHARACTERISTICS
|
value
|
Unit
|
Standard
|
|
FOAM - Flame Class Minimum Density/密度
|
0.9
|
g/cm³
|
-
|
|
UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
|
3.98
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3) / UL认可,94-5VA 阻燃等级(3)
|
3.98
|
mm
|
UL 94
|
|
Radiant Panel Listing / 辐射板清单
|
YES
|
-
|
UL Tested
|
|
Source GMD, last updated:07/01/1992
|
|
Parameter
|
|
Structural Foam Molding
|
value
|
Unit
|
|
Blowing Agent, Physical System
|
Nitrogen Gas
|
-
|
|
Blowing Agent, Chemical System
|
FNC30X
|
-
|
|
Concentration Range (Blowing Agent)
|
1 - 3
|
%
|
|
Recommended Concentration (Blowing Agent)
|
2
|
%
|
|
Drying Temperature / 干燥温度(Resin)
|
70 - 80
|
°C
|
|
Drying Time / 干燥时间(Resin)
|
2 - 4
|
hrs
|
|
Drying Time / 干燥时间(Resin, Cumulative)
|
8
|
hrs
|
|
Melt Temperature / 熔体温度
|
270 - 310
|
°C
|
|
Nozzle Temperature / 注嘴温度
|
270 - 305
|
°C
|
|
Front Temperature
|
270 - 305
|
°C
|
|
Middle Temperature
|
270 - 305
|
°C
|
|
Rear Temperature
|
230 - 260
|
°C
|
|
Mold Temperature / 模具温度
|
25 - 55
|
°C
|
|
放大图片