Lucet N109-LD
聚甲醛（POM）共聚物
|
比重
|
1.41
|
g/cm³
|
ASTM D792
|
|
熔流率（熔体流动速率） (190°C/2.16 kg)
|
9.0
|
g/10 min
|
ASTM D1238
|
|
收缩率 - 流动
|
1.8 到 2.1
|
%
|
ASTM D955
|
|
吸水率 (24 hr)
|
0.22
|
%
|
ASTM D570
|
|
洛氏硬度 (M 级)
|
82
|
|
ASTM D785
|
|
抗张强度 (屈服)
|
61.2
|
MPa
|
ASTM D638
|
|
伸长率 (断裂)
|
70
|
%
|
ASTM D638
|
|
弯曲模量
|
2600
|
MPa
|
ASTM D790
|
|
弯曲强度 (屈服)
|
98.0
|
MPa
|
ASTM D790
|
|
摩擦系数 (与自身 - 静态)
|
0.16
|
|
ASTM D1894
|
|
悬壁梁缺口冲击强度
|
|
|
ASTM D256
|
|
-40°C
|
49
|
J/m
|
|
|
23°C
|
69
|
J/m
|
|
|
载荷下热变形温度
|
|
|
ASTM D648
|
|
0.45 MPa, 未退火
|
160
|
°C
|
|
|
1.8 MPa, 未退火
|
110
|
°C
|
|
|
线形热膨胀系数 - 流动
|
1.0E-4
|
cm/cm/°C
|
ASTM D696
|
|
表面电阻率
|
1.0E+16
|
ohms
|
ASTM D257
|
|
体积电阻率
|
1.0E+14
|
ohms·cm
|
ASTM D257
|
|
介电强度
|
24
|
kV/mm
|
ASTM D149
|
|
介电常数 (1 MHz)
|
3.80
|
|
ASTM D150
|
|
耗散因数 (1 MHz)
|
7.0E-3
|
|
ASTM D150
|
|
耐电弧性 (3.18 mm)
|
240
|
sec
|
ASTM D495
|
|
UL 阻燃等级 (0.794 mm)
|
HB
|
|
UL 94
|
|
干燥温度
|
80.0 到 100
|
°C
|
|
|
干燥时间
|
3.0 到 6.0
|
hr
|
|
|
料筒后部温度
|
160 到 180
|
°C
|
|
|
料筒中部温度
|
180 到 200
|
°C
|
|
|
料筒前部温度
|
190 到 200
|
°C
|
|
|
射嘴温度
|
190 到 210
|
°C
|
|
|
加工（熔体）温度
|
190 到 200
|
°C
|
|
|
模具温度
|
60.0 到 80.0
|
°C
|
|
|
注塑压力
|
39.2 到 68.6
|
MPa
|
|
|
背压
|
3.92 到 7.84
|
MPa
|
|
|
螺杆转速
|
50 到 100
|
rpm
|
|
随货提供: 原厂物性表,开增值税发票，COC(合格证书),COA(产品证明),SGS报告,增值税发票及UL黄卡MSDS
郑重承诺:本公司所售原料均为原厂原包装正牌料,杜绝一切副牌料,水口料以次充好
运费说明：
1.支持物流，快递和货运 支持现金，银行转账。
2.本司原料低于500KG，不承担运费，订货500KG以上珠三角地区可送货上门 省外客户物流，快递或货运 不便之处敬请谅解!
3.选用物流或者快递的买家，请先确认当地是否有该物流或快递的营业网点。
4.原料到厂后，请不要拆外包装，应先仔细检查原料的外包装是否完好及原料型号是否与您所订购原料型号相匹配。
5.货物送达后，请当面检查，若物流过程中出现大量包装损坏及原料外漏的,请让物流人员出具证明并保存，并立即与我们联系。
6.我们承诺期限内发货，但对承运人效率无法作出保证，如果物流快递超出3天，货运超出5天，请联络我们协助查询。
7.买家也可以根据交易状态中填写的单号信息，自行联系承运方，以便第一时间获知详细信息。
8.本公司原料售后的注塑加工由客户负责，如需帮助，我公司工程部将竭尽所能与您共同协商处理。
|
放大图片
暂无相关下载