NORYL PPO EXNL1100物性表

TYPICAL PROPERTIES (1)
MECHANIC AL机械性能	value	Unit	Standard
Tensile Stress, yld, Type I, 10 mm/min	63	MPa	SABIC - Japan Method
Tensile Strain, brk, Type I, 10 mm/min	8	%	SABIC - Japan Method
Flexural Stress, yield, 6.4 mm	100	MPa	ASTM D 790
Flexural Modulus, 6.4 mm	4550	MPa	ASTM D 790
IMPACT	value	Unit	Standard
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C	34	J/m	ASTM D 256
THERMAL	value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火	104	°C	ASTM D 648
PHYSICAL	value	Unit	Standard
Specific Gravity/比重	1.22	-	ASTM D 792
Mold Shrinkage, flow (5)	0.4	%	SABIC Method
Mold Shrinkage, xflow (5)	0.4	%	SABIC Method
FLAME CHARACTERISTICS	value	Unit	Standard
UL Compliant, 94V-1 Flame Class Rating (3)(4)	1.5	mm	UL 94 by GE

Source GMD, last updated:2009/10/14

Processing

 

Parameter
Injection Molding	value	Unit
Drying Temperature / 干燥温度	90 - 95	°C
Drying Time / 干燥时间	3 - 4	hrs
Drying Time (Cumulative) / 干燥时间（累积的）	8	hrs
Maximum Moisture Content / 最大含湿量	0.02	%
Melt Temperature / 熔体温度	255 - 280	°C
Nozzle Temperature / 注嘴温度	255 - 280	°C
Front - Zone 3 Temperature / 前区3温度	245 - 280	°C
Middle - Zone 2 Temperature / 中区2温度	230 - 275	°C
Rear - Zone 1 Temperature / 后区1温度	220 - 270	°C
Mold Temperature / 模具温度	65 - 90	°C
Back Pressure / 背压	0.3 - 0.7	MPa
Screw Speed / 螺杆速度	20 - 100	rpm
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比	30 - 70	%
Vent Depth / 排气孔深度	0.038 - 0.051	mm