TYPICAL PROPERTIES (1)
|
|
MECHANICAL机械性能
|
value
|
Unit
|
Standard
|
|
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg
|
65
|
mg/1000cy
|
SABIC Method
|
|
Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min
|
55
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
|
50
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
|
5
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
|
30
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
|
2300
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
|
75
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
Hardness, H358/30 / 球压硬度，H358/30
|
100
|
MPa
|
ISO 2039-1
|
|
IMPACT
|
value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C
|
200
|
J/m
|
ASTM D 256
|
|
Izod IMPACT, notched, -40°C / 悬壁梁缺口冲击强度，-40°C
|
140
|
J/m
|
ASTM D 256
|
|
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度，80*10*4 +23°C
|
10
|
kJ/m²
|
ISO 180/1A
|
|
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度，80*10*4 -30°C
|
5
|
kJ/m²
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，23°C，C80*10*4 sp=62mm
|
10
|
kJ/m²
|
ISO 179/1eA
|
|
Charpy Impact, notched, 23°C
|
15
|
kJ/m²
|
ISO 179/2C
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，-30°C，C80*10*4 sp=62mm
|
5
|
kJ/m²
|
ISO 179/1eA
|
|
THERMAL
|
value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
148
|
°C
|
ASTM D 1525
|
|
Thermal Conductivity / 导热系数
|
0.22
|
W/m-°C
|
ISO 8302
|
|
CTE, 23°C to 80°C, flow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, xflow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate A/50 / 维卡软化温度 A级/50
|
145
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
135
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
|
140
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 热变形温度，0.45 MPa, 未退火, 100 mm 跨距
|
130
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度，1.8 MPa, 未退火, 100 mm 跨距
|
115
|
°C
|
ISO 75/Ae
|
|
PHYSICAL
|
value
|
Unit
|
Standard
|
|
Specific Gravity/比重
|
1.06
|
-
|
ASTM D 792
|
|
Water Absorption, 24 hours / 吸水率， 24小时
|
0.07
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 100°C / 吸水率，平衡，100°C
|
0.3
|
%
|
ASTM D 570
|
|
Mold Shrinkage on Tensile Bar, flow (2) / 收缩率，流动
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Density/密度
|
1.06
|
g/cm³
|
ISO 1183
|
|
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
|
0.23
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
|
0.06
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 280°C/5.0 kg
|
8
|
cm³/10 min
|
ISO 1133
|
|
ELECTRICAL
|
value
|
Unit
|
Standard
|
|
Dielectric Strength, shorttime, 3.2 mm
|
22
|
kV/mm
|
ASTM D 149
|
|
Volume Resistivity/体积电阻率
|
1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity, ROA / 表面电阻率
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, shorttime, 1.0mm
|
19
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity, 50/60 Hz / 相对介电常数，50/60 Hz
|
2.7
|
-
|
IEC 60250
|
|
Relative Permittivity, 1 MHz / 相对介电常数，1 MHz
|
2.6
|
-
|
IEC 60250
|
|
Dissipation Factor, 50/60 Hz / 耗散因素，50/60 Hz
|
0.002
|
-
|
IEC 60250
|
|
Dissipation Factor, 1 MHz / 耗散因素，1 MHz
|
0.001
|
-
|
IEC 60250
|
|
FLAME CHARACTERISTICS
|
value
|
Unit
|
Standard
|
|
UL Compliant, 94HB Flame Class Rating (3)(4)
|
1.65
|
mm
|
UL 94 by GE
|
|
Glow Wire Flammability Index / 灼热丝易燃指数 750°C, passes at
|
3.2
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index (LOI) / 极限氧指数
|
22
|
%
|
ISO 4589
|