TYPICAL PROPERTIES (1)
|
|
MECHANICAL机械性能
|
value
|
Unit
|
Standard
|
|
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg
|
30
|
mg/1000cy
|
SABIC Method
|
|
Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min
|
65
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min
|
55
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min
|
4
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min
|
10
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min
|
2600
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min
|
85
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
Hardness, H358/30 / 球压硬度，H358/30
|
100
|
MPa
|
ISO 2039-1
|
|
IMPACT
|
value
|
Unit
|
Standard
|
|
Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度，80*10*4 +23°C
|
10
|
kJ/m²
|
ISO 180/1A
|
|
Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度，80*10*4 -30°C
|
5
|
kJ/m²
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，23°C，C80*10*4 sp=62mm
|
10
|
kJ/m²
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，-30°C，C80*10*4 sp=62mm
|
5
|
kJ/m²
|
ISO 179/1eA
|
|
THERMAL
|
value
|
Unit
|
Standard
|
|
Thermal Conductivity / 导热系数
|
0.22
|
W/m-°C
|
ISO 8302
|
|
CTE, 23°C to 80°C, flow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, xflow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Ball Pressure Test, approximate maximum
|
145
|
°C
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate A/50 / 维卡软化温度 A级/50
|
165
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50
|
150
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120
|
155
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 热变形温度，0.45 MPa, 未退火, 100 mm 跨距
|
150
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度，1.8 MPa, 未退火, 100 mm 跨距
|
140
|
°C
|
ISO 75/Ae
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
105
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
85
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
105
|
°C
|
UL 746B
|
|
PHYSICAL
|
value
|
Unit
|
Standard
|
|
Mold Shrinkage on Tensile Bar, flow (2) / 收缩率，流动
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Density/密度
|
1.06
|
g/cm³
|
ISO 1183
|
|
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat)
|
0.25
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH)
|
0.07
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 300°C/5.0 kg
|
9
|
cm³/10 min
|
ISO 1133
|
|
ELECTRICAL
|
value
|
Unit
|
Standard
|
|
Volume Resistivity/体积电阻率
|
1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity, ROA / 表面电阻率
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, in oil, 0.8 mm / 耐电强度，在油中，0.8mm
|
33
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 1.6 mm / 耐电强度，在油中，1.6mm
|
26
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil, 3.2 mm / 耐电强度，在油中，3.2mm
|
16
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity, 50/60 Hz / 相对介电常数，50/60 Hz
|
2.8
|
-
|
IEC 60250
|
|
Relative Permittivity, 1 MHz / 相对介电常数，1 MHz
|
2.7
|
-
|
IEC 60250
|
|
Dissipation Factor, 50/60 Hz / 耗散因素，50/60 Hz
|
0.003
|
-
|
IEC 60250
|
|
Dissipation Factor, 1 MHz / 耗散因素，1 MHz
|
0.002
|
-
|
IEC 60250
|
|
FLAME CHARACTERISTICS
|
value
|
Unit
|
Standard
|
|
UL Recognized, 94V-1 Flame Class Rating (3) / UL认可,94V-1 阻燃等级(3)
|
0.97
|
mm
|
UL 94
|
|
UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)
|
3
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3) / UL认可,94-5VA 阻燃等级(3)
|
3
|
mm
|
UL 94
|
|
Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at
|
3.2
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index (LOI) / 极限氧指数
|
32
|
%
|
ISO 4589
|
放大图片