Low density polyethylene (LDPE) resins from LyondellBasell are thermoplastics made from the polymerization of ethylene in autoclave or tubular reactors at very high pressures. Unlike low-pressure polymerization technologies, high-pressure polymerization allows the co-polymerization of ethylene with polar comonomers, such as vinyl acetate or butyl acrylate. The polymer is characterized by a highly-branched polymer structure.
Purell PE 3020 K
特点：光学性能 刚性良好 刚性高 可加工性良好 可热封 耐化学性良好 良好的热封性
用途：医疗/护理用品 药物 薄膜
Purell PE 3020 K 物性表：
|
密度
|
0.928
|
g/cm³
|
ISO 1183
|
|
熔流率（熔体流动速率） (190°C/2.16 kg)
|
4.0
|
g/10 min
|
ISO 1133
|
|
拉伸模量
|
300
|
MPa
|
ISO 527-2
|
|
拉伸应力 (屈服)
|
13.0
|
MPa
|
ISO 527-2
|
|
摩擦系数 (吹塑薄膜)
|
> 0.80
|
|
ISO 8295
|
|
可供应的薄膜厚度
|
15 to 40 µm
|
|
|
|
抗张强度
|
|
|
ISO 527-3
|
|
MD : 50 µm, 吹塑薄膜
|
20.0
|
MPa
|
|
|
TD : 50 µm, 吹塑薄膜
|
17.0
|
MPa
|
|
|
伸长率
|
|
|
ISO 527-3
|
|
MD : 断裂, 50 µm, 吹塑薄膜
|
350
|
%
|
|
|
TD : 断裂, 50 µm, 吹塑薄膜
|
600
|
%
|
|
|
落锤冲击 (50 µm, 吹塑薄膜)
|
90
|
g
|
ASTM D1709
|
|
维卡软化温度
|
97.0
|
°C
|
ISO 306/A50
|
|
溶融温度（DSC）
|
114
|
°C
|
ISO 3146
|
|
光泽度
|
|
|
ASTM D2457
|
|
20°, 50.0 µm, 吹塑薄膜
|
> 80
|
|
|
|
60°, 50.0 µm, 吹塑薄膜
|
> 115
|
|
|
|
雾度 (50.0 µm, 吹塑薄膜)
|
< 7.0
|
%
|
ASTM D1003
|
|
Failure Energy 2 (50.0 µm)
|
55.0
|
J/cm
|
DIN 53373
|
供应利安德巴塞尔LDPE：
Purell 2007H
Purell 2410T
Purell PE 1810 E
Purell PE 1840 H
Purell PE 2420 F
Purell PE 3020 D
Purell PE 3020 H
Purell PE 3020 K
Purell PE 3040 D
Purell PE 3220 D
Purell PE3420F
主营系列：
1、通用塑料：ABS、PP、HDPE、LDPE、LLDPE、HIPS、GPPS、PVC等。
2、尼龙系列：PA6、PA66、PA11、PA12、PA46、PA6T、PA9T、透明尼龙、增强尼龙、阻燃尼龙、增强阻燃尼龙、超韧耐寒尼龙。
3、工程塑料：PMMA、PC、PPO、PPE、POM、PBT、PET、ASA、AES、CA等。
4、特殊塑料： LCP、PPS、PEI、PSF、PSU、PSO、PPA、TPX、PC/ABS、EVOH、PBT/PET、PC/PET、PA/PPO、PC/GF/PTFE、PEEK。
5、合成橡胶：TPU、TPE、TPEE、TPR、SBR、SEBS、TPV、EVA、SM、K胶、EVA 。
6、塑胶原料导电系列、抗静电系列、加铁氟龙系列、加铁氟龙加玻纤系列、加铁氟龙加碳纤系列、加碳纤系列等。
随货提供COA，SGS，UL黄卡，加工参数。欢迎您的来电！
联系电话：18826876991（戴小姐）
|
放大图片
暂无相关下载