TYPICAL PROPERTIES (1)
|
|
MECHANICAL/机械性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min
|
58
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min
|
49
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min
|
7.2
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min
|
28.1
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 50 mm/min
|
2860
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span
|
90
|
MPa
|
ASTM D 790
|
|
Flexural Stress, yld / 挠曲强度, 屈服 , 2.6 mm/min, 100 mm span
|
89
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span
|
2640
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 挠曲模量, 2.6 mm/min, 100 mm span
|
2420
|
MPa
|
ASTM D 790
|
|
Hardness，Rockwell / 洛氏硬度 R
|
119
|
-
|
ASTM D 785
|
|
Tensile Stress, yield / 抗张程度,屈服, 50 mm/min
|
57
|
MPa
|
ISO 527
|
|
Tensile Stress, break / 抗张程度,断裂, 50 mm/min
|
51
|
MPa
|
ISO 527
|
|
Tensile Strain, yield / 拉伸伸长,屈服, 50 mm/min
|
3.5
|
%
|
ISO 527
|
|
Tensile Strain, break / 拉伸伸长,断裂, 50 mm/min
|
17
|
%
|
ISO 527
|
|
Tensile Modulus / 拉伸模量, 1 mm/min
|
2700
|
MPa
|
ISO 527
|
|
Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min
|
95
|
MPa
|
ISO 178
|
|
Flexural Modulus / 挠曲模量, 2 mm/min
|
2550
|
MPa
|
ISO 178
|
|
IMPACT/冲击性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C
|
213
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度, -40°C
|
133
|
J/m
|
ASTM D 256
|
|
Gardner（加德纳冲击强度）, -30°C
|
25
|
J
|
ASTM D 3029
|
|
Gardner（加德纳冲击强度）, -40°C
|
5
|
J
|
ASTM D 3029
|
|
Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C
|
48
|
J
|
ASTM D 3763
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 +23°C
|
17
|
kJ/m²
|
ISO 180/1A
|
|
Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*4 -30°C
|
5
|
kJ/m²
|
ISO 180/1A
|
|
Charpy（简支梁缺口冲击强度） 23°C, V-notch（V型切口） Edgew 80*10*4 sp=62mm
|
17
|
kJ/m²
|
ISO 179/1eA
|
|
THERMAL/热性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
148
|
°C
|
ASTM D 1525
|
|
HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火）
|
131
|
°C
|
ASTM D 648
|
|
HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
117
|
°C
|
ASTM D 648
|
|
HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
|
137
|
°C
|
ASTM D 648
|
|
HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
126
|
°C
|
ASTM D 648
|
|
CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）
|
9.18E-05
|
1/°C
|
ASTM E 831
|
|
CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）
|
9.54E-05
|
1/°C
|
ASTM E 831
|
|
CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）
|
9.18E-05
|
1/°C
|
ISO 11359-2
|
|
CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）
|
9.54E-05
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50
|
140
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120
|
143
|
°C
|
ISO 306
|
|
HDT（热变形温度）/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
120
|
°C
|
ISO 75/Af
|
|
Relative Temp Index, Elec / 相对热指数， 电性能
|
105
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能
|
90
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能
|
105
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Specific Gravity / 比重
|
1.06
|
-
|
ASTM D 792
|
|
Water Absorption / 吸水率, 24 hours
|
0.06
|
%
|
ASTM D 570
|
|
Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收缩率, xflow（横向）, 3.2 mm
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 280°C/5.0 kgf
|
9.2
|
g/10 min
|
ASTM D 1238
|
|
Density / 密度
|
1.06
|
g/cm³
|
ISO 1183
|
|
Water Absorption / 吸水率, (23°C/sat)
|
0.23
|
%
|
ISO 62
|
|
Moisture Absorption / 吸水率, 平衡 (23°C / 50% RH)
|
0.06
|
%
|
ISO 62
|
|
Melt Volume Rate / 溶化体积流率, MVR at 280°C/5.0 kg
|
9
|
cm³/10 min
|
ISO 1133
|
|
ELECTRICAL/电气性能
|
value/值
|
Unit/单位
|
Standard/标准
|
|
Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm
|
21.6
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity / 相对介电常数, 50/60 Hz
|
2.65
|
-
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.0004
|
-
|
ASTM D 150
|
|
Arc Resistance, Tungsten / 耐电弧性 {PLC}
|
7
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition / 热丝引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高电压电弧起痕速率 {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS/火焰特性
|
value/值
|
Unit/单位
|
Standard/标准
|
|
UL Recognized, 94HB Flame Class Rating / 阻燃等级 (3)
|
1.47
|
mm
|
UL 94
|
|
CSA (See File for complete listing)
|
LS88480
|
File No.
|
CSA LISTED
|
|
Oxygen Index / 极限氧指数 (LOI)
|
22
|
%
|
ASTM D 2863
|
放大图片