| 详细介绍：
Celcon® LW90-S2
聚甲醛（POM）共聚物
产品说明:
Celcon® LW90-S2 is a preblended low wear formulation of M90 base polymer containing 2% silicone. This standard low friction, low wear product performs well in many applications including those involving intermittent motion.
|
比重
|
|
|
|
|
--
|
1.40
|
g/cm3
|
ASTM D792
|
|
--
|
1.38
|
g/cm3
|
ISO 1183
|
|
溶化体积流率（MVR） (190°C/2.16 kg)
|
8.40
|
cm3/10min
|
ISO 1133
|
|
收缩率
|
|
|
|
|
流动
|
2.2
|
%
|
ASTM D955
|
|
横向流动
|
1.8
|
%
|
ASTM D955
|
|
横向流量
|
1.6
|
%
|
ISO 294-4
|
|
流量
|
1.9
|
%
|
ISO 294-4
|
|
拉伸模量
|
2500
|
MPa
|
ISO 527-2/1A/1
|
|
抗张强度
|
|
|
|
|
屈服, 23°C
|
51.0
|
MPa
|
ASTM D638
|
|
屈服
|
56.0
|
MPa
|
ISO 527-2/1A/50
|
|
拉伸应变 (屈服)
|
10
|
%
|
ISO 527-2/1A/50
|
|
弯曲模量 (23°C)
|
2400
|
MPa
|
ISO 178
|
|
简支梁缺口冲击强度
|
|
|
ISO 179/1eA
|
|
-30°C
|
4.5
|
kJ/m2
|
|
|
23°C
|
7.0
|
kJ/m2
|
|
|
悬壁梁缺口冲击强度 (23°C)
|
5.3
|
kJ/m2
|
ISO 180/1A
|
|
载荷下热变形温度
|
|
|
|
|
1.8 MPa, 未退火
|
110
|
°C
|
ASTM D648
|
|
1.8 MPa, 未退火
|
94.0
|
°C
|
ISO 75-2/A
|
|
熔融温度
|
|
|
|
|
-- 3
|
166
|
°C
|
ISO 11357-3
|
|
--
|
165
|
°C
|
ASTM D3418
|
|
线形热膨胀系数
|
|
|
ISO 11359-2
|
|
流动
|
1.1E-4
|
cm/cm/°C
|
|
|
横向
|
1.2E-4
|
cm/cm/°C
|
|
|
体积电阻率
|
1.0E+14
|
ohms·cm
|
ASTM D257
|
|
干燥温度
|
80.0 到 100
|
°C
|
|
|
干燥时间
|
3.0
|
hr
|
|
|
料筒后部温度
|
170 到 180
|
°C
|
|
|
料筒中部温度
|
180 到 190
|
°C
|
|
|
料筒前部温度
|
180 到 190
|
°C
|
|
|
射嘴温度
|
190 到 200
|
°C
|
|
|
加工（熔体）温度
|
180 到 200
|
°C
|
|
|
模具温度
|
80.0 到 120
|
°C
|
|
|
注塑压力
|
60.0 到 120
|
MPa
|
|
|
注射速度
|
慢到中等
|
|
|
|
保压
|
60.0 到 120
|
MPa
|
|
|
背压
|
0.00 到 4.00
|
MPa
|
|
|
放大图片