金特塑胶长期供应PPS以下型号:
RTP Compounds 1387 HEC PPS RTP Company
RTP Compounds 1387 HM PPS RTP Company
RTP Compounds 1387 L PPS RTP Company
RTP Compounds 1387 P-1 PPS RTP Company
RTP Compounds 1387 P-1 TFE 10 PPS RTP Company
RTP Compounds 1387 SI PPS RTP Company
RTP Compounds 1387 SI 2 PPS RTP Company
RTP Compounds 1387 TFE 10 PPS RTP Company
RTP Compounds 1387 TFE 10 L PPS RTP Company
RTP Compounds 1387 TFE 13 SI 2 PPS RTP Company
RTP Compounds 1387 TFE 15 PPS RTP Company
RTP Compounds 1387 TFE 15 SI 2 PPS RTP Company
RTP Compounds 1387 TFE 5 PPS RTP Company
RTP Compounds 1389 PPS RTP Company
RTP Compounds 1389 HEC PPS RTP Company
RTP Compounds 1389 HM PPS RTP Company
RTP Compounds 1389 P-1 PPS RTP Company
RTP Compounds 1390 PPS RTP Company
RTP Compounds 1390 HM PPS RTP Company
RTP Compounds 1391 PPS RTP Company
RTP Compounds 1391 HM PPS RTP Company
RTP Compounds 1399 X 102903 J PPS RTP Company
PPS 日本油墨 FZ-3805-S2
原料物性描述:
英文名称：Phenylene sulfide
比重：1.36克/立方厘米
成型收缩率：0.7%
成型温度：300-330℃
PPS塑料，PPS塑料中文名叫做聚苯硫醚，英文名称是Phenylene sulfide。PPS塑料比重:1.36g/cm3 成型收缩率:0.7% 成型温度：300-330℃ PPS为塑性结晶性树脂，其结晶度约为65%，外观为白色或琥珀色。纯PPS的密度为1.3~1.35g/cm3,但很少单独使用,应用的PPS多为改性品级,如玻璃纤维增强、无机填充和碳纤维增强度，改性后的密度增大为1.60~1.68 g/cm3.
‧PPS 日本油墨 FZ-3805-S2
PPS的应用
PPS具有优良的耐高温性及高温机械性质优异的耐燃性、耐化学品性以及电气绝缘性而成为受到注目的耐高温工程塑胶。大日本油墨(DIC)提供多种等级的PPS(聚萃撑硫化物)包括交连型PPS及线型PPS的基本等级系列超韧系列合金与改质系列自润滑系列导电系列及电子元件封装系列等。适当的选择等级 DIC的PPS可适用于许多不同的应用产品。重要应用领域有电子/电气零件精密光电零件汽车零件以及特殊工业零件与机械零件等。 简介 PPS为聚萃撑硫化物[poly(phenylene sulfide)]的简称。 PPS通常是由对二氯萃与硫化纳在溶剂中聚合而得。 Cl-C6H4-Cl + Na2S ----> -(- C6H4-S- )n- + NaCl
PPS为半结晶聚合体。 PPS的玻璃转变温度(Tg)约为90°C而其熔点(Tm)约为280°C。高熔点使PPS具有承受高温的潜力。 芳香结构使PPS具有优良的热安定性。图1为PPS以TGA所测得的热重曲线。在氮气下PPS的热分解温度高于500°C。如图1所示在空气下PPS的热分解温度较之在氮气下有所下降但在450°C的高温下并无明显的重量损失。此表示PPS对于高温氧化有优异的耐受性。然而 PPS在氧气的存在下加热至高温并非完全无变化有一奇特的现象:交连反应(cross-linking)可能发生。